They get along just fine in the short run, but in the long run the nickel gets corroded...Originally Posted by Waterlogged
First I'm hearing of this?
If this were the case, there would be a whole lot more ppl screaming bloody murder. Fact is, copper and nickel get along just fine.
however, i really doubt this is erosion due to the abrasive force of the cooling fluid. theres no particles in water, and the flowrate is pretty low, even with a d5...
To this, there is only one proper response...
Circles SucQ!
If your annoyed by sigs telling you to put things in your sig, then put this in your sig
Bribery won't work on me...just say NO to AT!!!
To this, there is only one proper response...
http://en.wikipedia.org/wiki/Table_o...ode_potentials
i guess you learned how to read?
Why are they always........?
Guess you never heard of "nobility of metals" huh? Do yourself a favor and read this (Link), and educate yourself a bit please. The closer 2 metals are, the less of a problem there will be with corrosion...and, if you look at the chart, nickel and copper are bosom buddies. Another interesting tidbit you might want to read is here (Link).
Circles SucQ!
If your annoyed by sigs telling you to put things in your sig, then put this in your sig
Bribery won't work on me...just say NO to AT!!!