The galvanic table is for metal to metal contact in atmosphere under varying humid/salt conditions, and does not apply to oxidation/reduction for ions in solution. For metals that ionize, separated by a solution, it is oxidation/reduction reactions, ie SEP that governs corrosiveness.
For a nickel plated block and a silver coil in solution, there is no direct metal to metal contact, so again only SEP (standard electrode potential) applies. Silver is +0.8, nickel is -0.2, copper is +.2. Nickel will lose its electron (oxidation corrosion) to Silver (AG) that is not debatable. The only unknown is silver ions are only at ? 20 ppb concentration or so from a silver coil, and ? if enough to cause corrosion at significant rate, but no doubt corrosion/erosion of nickel will occur faster than if silver or copper were not used.
But again why I stick with just all copper, and only nickel plated fittings. I have never seen nickel plating corrosion of my fittings with pt nuke but there are not stagnant flow areas in fittings, but water blocks have localized areas of stagnant flow around seals (where narrow place between plexi and nickel), where ions can concentrate and cause localized crevice corrosion (again from oxidation/reduction reactions governed by SEP), which is what testing showed causes/starts the problem, and is evident in many of testing pics, +/- again subpar prepping and plating.
Which is why I just use all copper, pt nuke, and nickel fittings, then dont have to worry about anything corroding. Except my nickel fittings that are attached to radiator that do seem to corrode/erode some after 5+ years of use.
Last edited by rge; 05-08-2012 at 07:21 AM.
wouldent an ion charge reaction lead to positive moving to negative so the silver would migrate the nickle and even then you need the solution to be at about 70c. it would not really cause a problem unless you had a silver platted block, but i am not aware of any silver plated blocks with acrylic tops. i can only recall the EK one that was for biocide.
then there is also the problem with brass since it runs about -0.4 on the sep with tin at -1.4, so you rad would get the inside of your rad coated with the loose ions before anything else.
5930k, R5E, samsung 8GBx4 d-die, vega 56, wd gold 8TB, wd 4TB red, 2TB raid1 wd blue 5400
samsung 840 evo 500GB, HP EX 1TB NVME , CM690II, swiftech h220, corsair 750hxi
Any basic science book or any decent website on corrosion....quote from one "Current flows through the electrolyte to the more noble metal (cathode) and the less noble (anode) metal will corrode". So nickel, less noble than silver, will corrode (lose an electron). Also regarding need for solution temp of 70C ?????, maybe if your electroplating with time constraints, but heat just accelerates corrosion, it still occurs at our water temps. But since we cant even agree on basic physical/electrical concepts.
Last edited by rge; 05-08-2012 at 02:06 PM.